SYG-1500/HD-Li-GREASE
Product Description
This heavy-duty grease consists of a highly viscous mineral hydrocarbon oil (ISO VG 1500), special lithium soap and particularly effective EP/AW additives. It also contains solid lubricants (MoS2 and graphite) to ensure reliable operation under starved lubrication conditions. SYG-HD 1500 Li-GREASE is resistant to ageing and protects reliably against corrosion.
Applications
SYG-1500/HD-Li-GREASE was especially developed for large low-speed rolling bearings subject to high loads. It is typically applied to lubricate the bearings of rollers (spherical roller bearings) in roller presses, bowl mill and rotary crushers in the base material industry. The operating conditions of the roller bearings, i.e.
·
Low speed, n = 10-30
rpm
·
High load, P/C = 0.25
– 0.50.
·
Bearing temperature
approx. 50-70 °C
·
Shock and vibration
loads require heavy-duty grease with a high base oil viscosity and excellent
anti-wear properties, such as grease
like SYG-HD 1500 Li-GREASE. This grease is
also suitable for the lubrication of pivoting bearings and plain bearings
Ø Application notes
The ambient temperature should be ≥ 15 °C when SYG-HD 1500 Li-GREASE is
applied with an automatic greasing pump.
Typical Properties
PARAMETERS |
TESTMETHODS |
SPECIFICATIONS |
Color |
Black |
|
Density
at 20 °C |
approx. 0.92 g/cm³ |
|
Kinematic
viscosity, 40 °C |
ASTM D-445 |
approx. 1500 mm²/s |
Kinematic
viscosity,100°C |
ASTM D-445 |
approx. 60 mm²/s |
Drop
point, DIN ISO 2176 |
DIN ISO 2176 |
>= 180 °C |
Speed
factor (n x dm) |
approx. 100 000 mm/min |
|
Testing
of lubricating greases on FAG FE9 rolling bearing tester, speed: 3000 min-1,
axial load: 1500 N, temperature 150 °C, service life F50
|
DIN 51821 |
>= 100 h |
Rolling
bearing grease test FAG FE8, tapered roller bearing room temperature bearing
31312 A, 75 min-1 / 75kN,400 - 500h, rolling bearing wear. |
18 mg |
|
Rolling
bearing grease test FAG FE8, tapered roller bearing 31312 A, 75 min-1 / 80kN,
80 °C, no running-in, 400 - 500 h, wear of rolling element, |
<= 30 mg |
|
Compatibility
with elastomers, 72 NBR 902 ,168h/ 100°C,change in volume |
< 10 % |
|
Compatibility
with elastomers, 72 NBR 902 ,168h/ 100°C, hardness (Shore A) |
approx. -5 |